WHITE FUSED ALUMINA WFA F280


PRODUCT: WHITE FUSED ALUMINA                                                                          SIZE:FEPA 280   
         
White Fused alumina was made from the high quality alumina by melting above 2000 in the electric arc furnace and cooling. It is white with the main crystal phase α-Al₂O₃.
 
AVERAGE CHEMICAL COMPOSITION(TYPICAL)                  PHYSICAL PROPERTIES(TYPICAL)
 
Al₂O₃                                                                   ≥99.5%            Specific Gravity           ≥3.90g/cm³
Na₂O                                                                   ≤0.30%            Mohs Hardness                  9.0        
Fe₂O₃                                                                 ≤0.06%             Bulk Density          1.75-1.95g/cm³                          
SiO₂                                                                    ≤0.05%           Melting Point                 2250℃
CaO                                                                    ≤0.05%            Refractoriness                2100℃
MgO                                                                    ≤0.03%
K₂O                                                                    ≤0.02%
LOI                                                                      ≤0.10%
 
PARTICLE SIZE DISTRIBUTION
                    
                                                                           STANDARD VALUE(um)
D3                                                                                      ≤59
D50                                                                                36.5±1.5
D94                                                                                    ≥22
 
MAIN APPLICATIONS
 
--Wet and dry blast media,grinding and polishing etc
--Bonded Abrasives and Coated abrasives
--Floor/Wall laminates,Wear-resistant
--Ceramic and Tiles,Ceramic filter plate,ceramic membrane etc
--Grinding wheels,Cup wheels,Whetstone,polishing pads etc
...
PACKAGING:25kgs PVC bags+1MT big bag